背板-Cybrid KPF
產(chǎn)品詳細介紹
產(chǎn)品特點
■ High resistance to heat and humidity
■ Excellent Sand Falling Test
■ Excellent partial discharge
■ High Inner Layer Reflectivity
■ Excellent UV Blocking
■ Excellent Thermal Conductive
■ High Water Barrier
■ Easy to Rework
產(chǎn)品規(guī)格
| Specification | Unit | Cynagard 205A | Cynagard 215A | Cynagard 225A | Standard | |
| Product thickness | um | 295.0±10% | 300.5±10% | 300.5±10% | ASTM E252 | |
| Tensile strength（MD/TD） | MPa | MD≥100 TD≥100 | MD≥100 TD≥100 | MD≥100 TD≥100 | ASTM D-882 | |
| Elongation of break（MD/TD） | % | MD≥100 TD≥80 | MD≥100 TD≥80 | MD≥100 TD≥80 | ASTM D-882 | |
| Heat shrinkage (MD/TD) 150℃*30min | % | ≤1.5 | ≤1.5 | ≤1.5 | ASTM D1204 | |
| PVDF/PET peel strength | N/cm | ≥4 | ≥4 | ≥4 | ISO 8510 | |
| Coating/PET adhesion | Level | 0 | 0 | 0 | ISO 2409 (Cross-Cut Method) | |
| BS/EVA peel strength | N/cm | ≥40 | ≥40 | ≥40 | ASTM D903 | |
| Inner layer reflectivity | % | ≥80 | ≥80 | ≥80 | ASTM E1164 | |
| Falling Sand Test | L | ≥100 | ≥100 | ≥100 | ASTM D968 | |
| Water Vapor transsmision 38℃ 90%RH (IR) | g/m2 .day | ≤2.0 | ≤2.0 | ≤2.0 | ISO15106-3 | |
| Adhesion to potting/sealant | Visual | Cohesive Failure of potting/sealant | Cohesive Failure of potting/sealant | Cohesive Failure of potting/sealant | ASTM D903 | |
| Breakdown Voltage | KV | ≥16 | ≥16 | ≥16 | ASTM D-149 | |
| Partial discharge | VDC | ≥1000 | ≥1000 | ≥1000 | IEC 60664-1 (TüV Rheinland Certification) | |
| TI | ℃ | 120 | 120 | 120 | IEC60216 (TüV Rheinland Certification) | |
| FSI | — | ＜100 | ＜100 | ＜100 | ASTM E 162 (TüV Rheinland Certification) | |
| Boiled① （24H） | PVDF/PET peel strength | N/cm | ≥3.5 | ≥3.5 | ≥3.5 | ISO 8510 |
| Coating/PET adhesion | Level | 0 | 0 | 0 | ISO 2409 (Cross-Cut Method) | |
| DH② （1000H） | Yellow index | Δb | ＜4 | ＜4 | ＜4 | ASTM E313 |
| PVDF/PET peel strength | N/cm | ≥3.5 | ≥3.5 | ≥3.5 | ISO 8510 | |
| Coating/PET adhesion | Level | 0 | 0 | 0 | ISO 2409 (Cross-Cut Method) | |
| UV③ （90KWH） | Yellow index | Δb | ＜4 | ＜4 | ＜4 | ASTM E313 |
| PVDF/PET peel strength | N/cm | ≥3.5 | ≥3.5 | ≥3.5 | ISO 8510 | |
| Coating/PET adhesion | Level | 0 | 0 | 0 | ISO 2409 (Cross-Cut Method) | |
| TC④ （200） | Yellow index | Δb | ＜4 | ＜4 | ＜4 | ASTM E313 |
| PVDF/PET peel strength | N/cm | ≥3.5 | ≥3.5 | ≥3.5 | ISO 8510 | |
| Coating/PET adhesion | Level | 0 | 0 | 0 | ISO 2409 (Cross-Cut Method) | |
| HF⑤ （10） | Yellow index | Δb | ＜4 | ＜4 | ＜4 | ASTM E313 |
| PVDF/PET peel strength | N/cm | ≥3.5 | ≥3.5 | ≥3.5 | ISO 8510 | |
| Coating/PET adhesion | Level | 0 | 0 | 0 | ISO 2409 (Cross-Cut Method) | |
Remark:Samples treated in ①boiled water ② 85%/85%RH.③60℃④－40℃～85℃⑤－40℃～85℃,85%RH